SikaQuick®-1000

SikaQuick®-1000

RAPID-HARDENING REPAIR MORTAR WITH EXTENDED WORKING TIME

SikaQuick®-1000 is a 1-component, rapid-hardening, early-strength gaining, cementitious, patching material for concrete.

  • Specifically suited for hot weather applications when extended working time is required
  • Rapid hardening as defined by ASTM C928
  • Can be used with Sikacem® Accelerator for cold conditions, increased early strengths and reduced curing time
  • Compatible with Sikafloor®, SikaBond®, and Sika® AcouBond systems
 
  • Allows application of an epoxy coating within 6 hours
  • Freeze/thaw resistant
  • Easy to use; economical patching and labour saving material
  • Contains no added chlorides
  • Formulated with inert, non-reactive aggregates to eliminate potential Alkali-Aggregate Reactivity (AAR).
  • Open to foot traffic in 4 hours, to vehicle traffic in 6 hours [+23 °C (73 °F)]
  • Easily applied to clean, sound substrates
  • Not a vapour barrier
  • Product recognized by the British Columbia Ministry of Transportation (BC MoT)
  • Meets CFIA and USDA requirements for use in food plants
SikaQuick®-1000
Contact
Product Data Sheet Safety Data Sheet Show all documents

Usage

  • Use on grade, above and below grade on concrete
  • Highway overlays and repairs
  • Structural repair material for concrete roadways, parking structures, bridges, dams and ramps
  • Full depth patching repairs
  • Horizontal repairs of concrete and mortar

Advantages

  • Specifically suited for hot weather applications when extended working time is required
  • Rapid hardening as defined by ASTM C928
  • Can be used with Sikacem® Accelerator for cold conditions, increased early strengths and reduced curing time
  • Compatible with Sikafloor®, SikaBond®, and Sika® AcouBond systems
 
  • Allows application of an epoxy coating within 6 hours
  • Freeze/thaw resistant
  • Easy to use; economical patching and labour saving material
  • Contains no added chlorides
  • Formulated with inert, non-reactive aggregates to eliminate potential Alkali-Aggregate Reactivity (AAR).
  • Open to foot traffic in 4 hours, to vehicle traffic in 6 hours [+23 °C (73 °F)]
  • Easily applied to clean, sound substrates
  • Not a vapour barrier
  • Product recognized by the British Columbia Ministry of Transportation (BC MoT)
  • Meets CFIA and USDA requirements for use in food plants

Packaging

25 kg (55 lb) bag

Colour

Concrete Grey

Product Details

Sustainability / Certifications / Approvals

ENVIRONMENTAL INFORMATION

  • Conformity with LEED®v4 MR Credit (Option 1): Building Product Disclosure and Optimization - Environmental Product Declarations
  • Conformity with LEED®v4 MR Credit (Option 1): Building Product Disclosure and Optimization - Material Ingredients
Product Information

Shelf Life

12 months in original, unopened packaging.

 

Storage Conditions

Stored (unopened) in a dry place at temperatures ranging between +5 °C and +32 °C (41 °F and 89 °F). For best results, condition product at temperatures between +18 °C and + 29 °C (65 °F and 84 °F) before using.
Technical Information

Compressive Strength

1 day30 MPa (4 350 psi)
7 days40 MPa (5 800 psi)
28 days50 MPa (7 250 psi)

* Compressive Stength (tested with SikaCem® Accelerator), ASTM C109

Temperature

Dosage

12 hours

1 day

2 days

28 days

-5 oC (23 oF)

1 bottle (150 mL)

15 MPa (2175 psi)19 MPa (2755 psi) 26 MPa (3770 psi)-
-5 oC (23 oF)

2 bottles (300 mL)

17 MPa (2465 psi)19 MPa (2755 psi)27 MPa (3916 psi)-

0 oC (32 oF)

1 bottle (150 mL)

23 MPa (3335 psi)

35 MPa (5076 psi)

41 MPa (5946 psi)

62 MPa (8992 psi)

0 oC (32 oF)

2 bottles (300 mL)

29 MPa (4206 psi)

43 MPa (6236 psi)

48 MPa (6961 psi)

69 MPa (10 007 psi)

10 oC (50 oF)

1 bottle (150 mL)

30 MPa (4350 psi)40 MPa (5800 psi)45 MPa (6526 psi)68 MPa (9862 psi)
10 oC (50 oF)

2 bottles (300 mL)

36 MPa (5221 psi)45 MPa (6526 psi)50 MPa (7250 psi)70 MPa (10 152 psi)
23 oC (73 oF)

1 bottle (150 mL)

42 MPa (6091 psi)48 MPa (6961 psi)52 MPa (7541 psi)68 MPa (9862 psi)

23 oC (73 oF)

2 bottles (300 mL)

48 MPa (6961 psi)

53 MPa (7687 psi)

54 MPa (7832 psi)

70 MPa (10 152 psi)

*All moulds, mixing tools and powder components were pre-conditioned to the test temperatures. Prepared test specimens were cast and then cured at the indicated test temperatures until the time of testing. Liquid/solids ratio (water + Sikacem® Accelerator/SikaQuick®-1000) = 0.115; [2.87 L (0.75 US gal.) of liquid per 25 kg (55 lb) bag of SikaQuick®-1000].

Modulus of Elasticity in Compression

28 days32.7 GPa (4.7 x 106 psi)

Tensile Strength in Flexure

28 days

8.0 MPa (1160 psi)

Splitting Tensile Strength

28 days

6.0 MPa (870 psi)

Shear Adhesion Strength

28 days

15.5 MPa (2250 psi)

* Mortar scrubbed into substrate at +23 °C (73 °F) / 50 % r.h.

Pull-Out Resistance

28 days

> 2.0 MPa (290 psi) Substrate failure

Shrinkage

28 days

0.07 %

Freeze thaw resistance

300 cycles

98 %

Freeze Thaw De-Icing Salt Resistance

50 cycles

0.39 kg/m2 (0.08 lb/ft2)

Application

Application Information

Mixing Ratio

2.6 L to 2.87 L (0.7 - 0.75 US gal.) of water per bag

Layer Thickness

Min.

Max.

Neat

6 mm (1/4 in.)

50 mm (2 in.)

Extended

25 mm (1 in.)

150 mm (6 in.)

  • Do not feather edge

Product Temperature

+18 °C to +29 °C (65 °F to 84 °F)

Ambient Air Temperature

+7 °C to +30 °C (44 °F to 86 °F)

Substrate Temperature

+7 °C to +30 °C (44 °F to 86 °F)

Pot Life

 Approx. 30 minutes after adding powder to the water

Initial Set Time

~ 45 - 65 min

(ASTM C266)

Final Set Time

~ 55 - 100 min

(ASTM C266)
Consumption

Yield

Approx. 13 L (0.459 ft3). When extended with 11 kg (24 lb) of 10 mm (3/8 in) aggregate, yield is approx. 17 L (0.6 ft3).
Application steps

MIXING

Mechanically mix in an appropriately sized mortar mixer. Wet down all tools and mixer to be used. Start with 2.6 L (0.7 US gal.) of clean potable water added to the mixing vessel. Add one bag of SikaQuick®-1000 while continuing to mix. Add up to another 270 mL (9.0 US fl. oz) of additional water to achieve desired consistency. For application exceeding 25 mm (1 in) in depth, add 11 kg (24 lb) of 10 mm (3/8 in) coarse aggregate.The aggregate must be non-reactive (as per ASTM C1260, C227, and C289), clean, well graded, saturated surface dry, have low absorption, high density and comply with ASTM C33, size number 8 per table 2. Note: Do not overwater the mix. This may cause excessive bleeding and retardation and will reduce the strength and performance of the material.

APPLICATION

A scrub coat should be applied prior to placement of mortar. Apply a 3 mm (1/8 in) thick scrub coat of SikaQuick®-1000 into the substrate, filling all pores, voids and edges. Onto the fresh scrub coat, force the mortar against the edge of the repair area or onto the resurfacing site, working towards the centre and observing minimum and maximum layer thicknesses. After filling the repair, screed off excess. Allow concrete to set to desired stiffness, then finish the surface. If a smoother finish is desired, use a magnesium float. Mixing, placing and finishing should not exceed 30 minutes maximum. To control setting times, cold water should be used in hot weather and hot water in cold weather.

CURING TREATMENT

Protect newly applied material from rain for at least four (4) hours. To prevent from freezing, cover with insulating material. If necessary, cure using Sika® Florseal® WB-18 & -25, which meets ASTM C309 requirements. Note: Do not moist/wet cure.

CLEAN UP

Clean all tools and equipment immediately after use with water. Once hardened, material can only be removed manually or mechanically. 